| − | microstructure of 1930s K Zildjian alloy from Turkey. B22 with a higher beta and lower alpha phase content. Nice clean microstrucure. Sample contains no silver, but does have Sulfur which might be from fire refined raw copper. The Iron is from the casting mold. Generally B22 with remarkably low contamination. | + | microstructure of 1930s K Zildjian alloy from Turkey. Lab notes: B22 with a higher beta and lower alpha phase content. Nice clean microstrucure. Sample contains no silver, but does have Sulfur which might be from fire refined raw copper. The Iron is from the casting mold. Generally B22 with remarkably low contamination. |
Revision as of 09:43, 17 June 2019
Summary
microstructure of 1930s K Zildjian alloy from Turkey. Lab notes: B22 with a higher beta and lower alpha phase content. Nice clean microstrucure. Sample contains no silver, but does have Sulfur which might be from fire refined raw copper. The Iron is from the casting mold. Generally B22 with remarkably low contamination.
File history
Click on a date/time to view the file as it appeared at that time.
| Date/Time | Thumbnail | Dimensions | User | Comment | |
|---|---|---|---|---|---|
| current | 19:07, 7 October 2021 |  | 1,858 × 742 (1.33 MB) | Type85 (talk | contribs) | |
| 17:38, 14 June 2019 |  | 929 × 371 (479 KB) | Zenstat (talk | contribs) | microstructure of 1930s K Zildjian alloy from Turkey |
- You cannot overwrite this file.
File usage
The following page uses this file: